SAKATA 3D PLA HR-870 filament is suitable for all consumer-grade 3D FDM/FFF printers. This filament delivers improved heat-resistance and high impact strength to 3D printed parts. SAKATA 3D HR-870 Filament achieves thermal and mechanical properties similar to ABS while offering an alternative to styrenic-based material. It provides excellent 3D printing characteristics such as precise detail, good adhesion to build plates, less warping and curling, and low odour. Made in Spain by POLIMERSIA GLOBAL S.L.
Specific gravity: 1.22 g/cm3
Net Filament Weight: 1kg
Tensile strength:40 MPa
Tensile modulus: 2,865 MPa
Flexural strength: 73 MPa
Flexural modulus: 2,414 MPa
Notched Izod impact: 233 J/m
Heat distortion temperature: 75-85 ºC
(1) All 3D printed parts printed at 100% infill and annealed at 110ºC/20 min.
Nozzle temp.: 205-225 ºC
Bed temp.: Not needed (50-70ºC optional)
Fan speed % 100
Layer height: 0.1-0.3 mm
Shell thickness: 1.2 mm
Print speed mm/s Up to 120 mm/s
Annealing temperature: 110-120 ºC
White, Orange, Grey, Silver, Black, Natural